3505MC WIRE AND CABLE
- ExxonMobil Chemical
You`ll need an account to perform this action. Don't worry. It's free!
Sign UpEnable™ 3505MC performance polymer resin is an ethylene 1-hexene copolymer. It can be employed in medium and high density jacketing. It has a
good balance of mechanical strength, abrasion and strong environmental stress crack resistance (ESCR). Sufficient carbon black or UV stabilizer should be added to
meet cable jacketing specifications.
You`ll need an account to add a review. Don't worry. It's free!
Sign UpYou`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Product Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Physical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Density | 0.935 | gm/cm³ | ASTM D1505 | - | - |
Melt Flow Index | 0.50 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
Durometer Hardness | 54 | EXXONMOBIL Method | - | - |
Mechanical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Tensile strength at Yield | 19 | MPa | EXXONMOBIL Method | (2.0 in/min(50mm/min)) | - |
Tensile strength at Break | 39 | MPa | EXXONMOBIL Method | (2.0 in/min(50mm/min)) | - |
Elongation @ Yield | 10 | % | EXXONMOBIL Method | (2.0 in/min(50mm/min)) | - |
Elongation @ Break | 790 | % | EXXONMOBIL Method | (2.0 in/min(50mm/min)) | - |
Flexural Modulus | 550 | MPa | EXXONMOBIL Method | (1% Secant Procdure A, 0.0051 in/min(1.3mm/min)) | - |
Environmental Stress - Cracking Resistance (ESCR) : @10% Igepal Soln (F₅₀) | >1000 | Hours | EXXONMOBIL Method | ( Condition B,10% legpal,F50) | - |
Thermal properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Peak Melting Temperature | 123 | °C | EXXONMOBIL Method | - | - |
VICAT Softening Point | 120 | °C | EXXONMOBIL Method | - | - |
Electrical properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Volume Resistivity | 7.5E+14 | Ωm | IEC 62631-3-1 | (500 V) | - |
Relative Permittivity | 2.28 | IEC 62631-2-1 | (1 MHz) | - | |
Dissipation factor | 1.3E-4 | IEC 62631-2-1 | (1 MHz) | - |
Legal Statement:
Tris(nonylphenol)phosphite (TNPP) CAS# 26523-78-4 is not intentionally used by ExxonMobil in this product. Although this product is not routinely tested for its presence, based on product composition knowledge this substance is not expected to be present. However, the fact that this substance is not intentionally used by ExxonMobil in this product does not exclude that trace levels of this substance may be present as a result of the specific characteristics of the raw materials and/or of the manufacturing process.
This product is not intended for use in medical applications and should not be used in any such applications.
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
Processing Statement:
Film (1 mil / 25.4 micron) made on a 2.5 inch (63.5 mm) blown film line with a 2.5:1 blow-up ratio, a melt temperature of 380- 400°F (193 - 204°C), a 30 mil (0.76
mm) die gap at a rate of 10 lbs/hr/in die circumference (1.79 kg/hr/cm).
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Plastic Generic Family | Polyethylene (PE) |
---|---|
Description | Legal Statement: Tris(nonylphenol)phosphite (TNPP) CAS# 26523-78-4 is not intentionally used by ExxonMobil in this product. Although this product is not routinely tested for its presence, based on product composition knowledge this substance is not expected to be present. However, the fact that this substance is not intentionally used by ExxonMobil in this product does not exclude that trace levels of this substance may be present as a result of the specific characteristics of the raw materials and/or of the manufacturing process. This product is not intended for use in medical applications and should not be used in any such applications.
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
Processing Statement: Film (1 mil / 25.4 micron) made on a 2.5 inch (63.5 mm) blown film line with a 2.5:1 blow-up ratio, a melt temperature of 380- 400°F (193 - 204°C), a 30 mil (0.76 mm) die gap at a rate of 10 lbs/hr/in die circumference (1.79 kg/hr/cm).
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability. |