Escor™ 5080 resin is an ethylene acrylic acid copolymer characterized by high melt index and 10 wt% acrylic acid comonomer content. Escor™ 5080 resin
easily combines processing and adhesion to polar materials. It can be formulated and UV-stabilized for use in outdoor applications.
You`ll need an account to add a review. Don't worry. It's free!
Sign Up
You`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Technical data sheetProduct Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Physical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Density | 0.937 | gm/cm³ | ASTM D1505 | - | - |
| Melt Flow Index | 30 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
Thermal properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Peak Melting Temperature | 95 | °C | EXXONMOBIL Method | - | - |
| VICAT Softening Point | 71 | °C | ASTM D1525 | - | - |
Additional Information
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Acrylic Acid Content | 10 | wt % | EXXONMOBIL Method | - | - |
Legal Statement:
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement:
Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D4703 Procedure C (Tensile ASTM D638 : Type IV dumbbell, Hardness ASTM D2240 : 3 plied up disks) and 2 plied up 2 mm (157 mil) for Vicat. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. Escor™ resin should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE preferably with a lower melt flow than the Escor™ grade in use or a suitable cleaning compound before shutdown. Never shutdown the equipment with Escor™ resin.
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
| Plastic Generic Family | Polyethylene (PE) |
|---|---|
| Description | Legal Statement: Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB). This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement:
Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D4703 Procedure C (Tensile ASTM D638 : Type IV dumbbell, Hardness ASTM D2240 : 3 plied up disks) and 2 plied up 2 mm (157 mil) for Vicat. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. Escor™ resin should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE preferably with a lower melt flow than the Escor™ grade in use or a suitable cleaning compound before shutdown. Never shutdown the equipment with Escor™ resin.
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
|