Escor™ 5110 resin is primarily intended for high speed, low coating weight extrusion coating and extrusion lamination. Escor™ 5110 resin offers the following
advantages: excellent adhesion to polar substrates, aluminum foil, polyamide films, metallized films, papers, iron, steel, and glass; high bond resistance when used to
pack acidic food products; very low sealing and hot tack initiation temperature; very high hot tack peak force.
You`ll need an account to add a review. Don't worry. It's free!
Sign Up
You`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Technical data sheetProduct Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Physical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Density | 0.939 | gm/cm³ | ASTM D1505 | - | - |
| Melt Flow Index | 14 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
Mechanical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Draw Down @35 rpm | 460 | m/min | EXXONMOBIL Method | (Constant output at 35 rpm, 536°F(280°C )) | - |
Thermal properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Peak Melting Temperature | 95 | °C | EXXONMOBIL Method | - | - |
Additional Information
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Acrylic Acid Content | 11.0 | wt % | EXXONMOBIL Method | - | - |
| Neck In (164 ft/min(50 m/min) | 18 | cm | EXXONMOBIL Method | (Constant output at 35 rpm, 536°F (280°C)) | - |
| Neck In (328 ft/min(100 m/min) | 8.1 | cm | (Constant output at 35 rpm, 536°F (280°C)) | - |
Legal Statement:
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement:
Typical values obtained on a pilot coextrusion coating line at ExxonMobil Europe Technical Center, at an air gap of 170 mm (6.69 in). Excellent results are obtained in extrusion coating at 260°C to 280°C (500 - 536 °F) temperature range. Processing temperatures above 300°C (572 °F) may cause resin degradation. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. Escor™ resin should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
| Plastic Generic Family | Polyethylene (PE) |
|---|---|
| Description | Legal Statement: Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB). This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement:
Typical values obtained on a pilot coextrusion coating line at ExxonMobil Europe Technical Center, at an air gap of 170 mm (6.69 in). Excellent results are obtained in extrusion coating at 260°C to 280°C (500 - 536 °F) temperature range. Processing temperatures above 300°C (572 °F) may cause resin degradation. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. Escor™ resin should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
|