HPA 020 is a high molecular weight HDPE resin, characterized by an excellent balance of rigidity, ESCR and impact strength.
You`ll need an account to add a review. Don't worry. It's free!
Sign Up
You`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Technical data sheetProduct Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Physical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Density | 0.952 | gm/cm³ | ASTM D1505 | - | - |
| Melt Mass Flow Rate | 0.35 | gm/10 min | ASTM D1238 | - | - |
| Durometer Hardness | 61 | ASTM D2240 | - | - | |
| High Load Melt Index | 9.0 | gm/10 min | ASTM D1238 | - | - |
Mechanical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Tensile Modulus | 1000 | MPa | ASTM D638 | (0.20 in/min (5.0 mm/min) | - |
| Tensile Stress | 14 | MPa | ASTM D638 | at 100% | 2.0 in/min (50 mm/min) |
| Tensile strength at Yield | 21 | MPa | ASTM D638 | 2.0 in/min (50 mm/min) | - |
| Elongation @ Break | >100 | % | ASTM D638 | 2.0 in/min (50 mm/min) | - |
| Environmental Stress - Cracking Resistance (ESCR) : @10% Igepal Soln (F₅₀) | 330 | Hours | ASTM D1693 | - | - |
| Environmental Stress - Cracking Resistance (ESCR) | >600 | Hours | ASTM D1693 | 100% lgepal | - |
| Izod Impact Strength, Notched | 18 | KJ/m² | ISO 180/1A | - | - |
Thermal properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| VICAT Softening Point | 126 | °C | ASTM D1525 | - | - |
LEGAL STATEMENT:
This product is not intended for use in food contact application.
This product is not intended for use in medical applications and should not be used in any such applications.
PROCESSING STATEMENT:
The molded properties have been measured on compression molded sheets, prepared according to ASTM D4703 and ASTM D 638. ASTM D 638: Specimen type T1 / thickness 3 mm (118 mil); tensile modulus : speed of testing 5 mm/min (197 mil/min); tensile strength at yield and elongation at break: speed of testing 50 mm/min (1970 mil/min). ASTM D1693: Conditions B, F50, 10 % Igepal and 100 % Igepal
NOTES:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability
| Plastic Generic Family | Polyethylene (PE) |
|---|---|
| Description | LEGAL STATEMENT: This product is not intended for use in food contact application. This product is not intended for use in medical applications and should not be used in any such applications.
PROCESSING STATEMENT: The molded properties have been measured on compression molded sheets, prepared according to ASTM D4703 and ASTM D 638. ASTM D 638: Specimen type T1 / thickness 3 mm (118 mil); tensile modulus : speed of testing 5 mm/min (197 mil/min); tensile strength at yield and elongation at break: speed of testing 50 mm/min (1970 mil/min). ASTM D1693: Conditions B, F50, 10 % Igepal and 100 % Igepal
NOTES: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability |