HTA 108 is a homopolymer HDPE film grade designed to improve stiffness and barrier in coextrusion or in PE blends. When blended with LLDPE or metallocene
LLDPE, HTA 108 improves their processability.
You`ll need an account to add a review. Don't worry. It's free!
Sign Up
You`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Technical data sheetProduct Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Film Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Tensile Strength at Break MD | 60 | MPa | ASTM D882 | - | - |
| Tensile Strength at Break TD | 31 | MPa | ASTM D882 | (20 in/min(500mm/min)) | - |
| Elongation at Break MD | 510 | % | ASTM D882 | (20 in/min(500mm/min)) | - |
| Elongation at Break TD | 2 | % | ASTM D882 | (20 in/min(500mm/min)) | - |
| Secant Modulus MD - 1% Secant | 1200 | MPa | ASTM D882 | - | - |
| Secant Modulus TD - 1% Secant | 1700 | MPa | ASTM D882 | - | - |
| Elmendorf Tear Strength MD | 10 | gm | ASTM D1922 | - | - |
| Elmendorf Tear Strength TD | 200 | gm | ASTM D1922 | - | - |
Physical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Density | 0.961 | gm/cm³ | ASTM D1505 | - | - |
| Melt Flow Index | 0.70 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
| Melt Mass Flow Rate | 46 | gm/10 min | ASTM D1238 | - | - |
Impact Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Dart Drop Impact | < 30 | gm | ASTM D 1709/A | - | - |
Thermal properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| VICAT Softening Point | 127 | °C | ASTM D1525 | - | - |
ADDITIONAL INFORMATION:
HTA108 can be added to LDPE, LLDPE or mLLDPE films to increase stiffness when high transparency is not mandatory.
LEGAL STATEMENT:
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB). This product is not intended for use in medical applications and should not be used in any such applications.
PROCESSING STATEMENT:
The test specimens for Vicat Softening Point were prepared using ASTM D 4703. All film properties have been measured on 25 µm (0.98 mil) thick films (BUR of 2.5 : 1, pocket extrusion at 200°C / 392°F). Properties of coextruded films and blends can be found in the HTA108 Fact Sheet.
NOTES:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability
| Plastic Generic Family | Polyethylene (PE) |
|---|---|
| Description | ADDITIONAL INFORMATION: HTA108 can be added to LDPE, LLDPE or mLLDPE films to increase stiffness when high transparency is not mandatory.
LEGAL STATEMENT: Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB). This product is not intended for use in medical applications and should not be used in any such applications.
PROCESSING STATEMENT: The test specimens for Vicat Softening Point were prepared using ASTM D 4703. All film properties have been measured on 25 µm (0.98 mil) thick films (BUR of 2.5 : 1, pocket extrusion at 200°C / 392°F). Properties of coextruded films and blends can be found in the HTA108 Fact Sheet.
NOTES: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability
|