ExxonMobil™ LLDPE LL 8446.21
- ExxonMobil Chemical
You`ll need an account to perform this action. Don't worry. It's free!
Sign UpLL 8446 is a linear low density butene copolymer designed to offer excellent processability, whiteness, and fast grinding rate. This UV stabilized resin is ideally
suited for applications that require excellent dimensional control and low warpage.
You`ll need an account to add a review. Don't worry. It's free!
Sign UpYou`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Product Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Physical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Density | 0.936 | gm/cm³ | ASTM D1505 | - | - |
Melt Flow Index | 5.0 | gm/10 min | ASTM D1238 | - | - |
Mechanical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Tensile strength at Yield | 17 | MPa | ASTM D638 | - | - |
Tensile Stress | 17 | MPa | (AT YIELD) | - | |
Tensile Strain | 10 | % | (AT YIELD) | - | |
Flexural Modulus | 730 | MPa | ASTM D790B | - | - |
Flexural Modulus | 700 | MPa | - | - | |
Environmental Stress - Cracking Resistance (ESCR) : @10% Igepal Soln (F₅₀) | 30 | Hours | ASTM D1693 | (0.0787 in (2.00 mml),10% legpal,F50) | - |
Environmental Stress - Cracking Resistance (ESCR) : @10% Igepal Soln (F₅₀) | 20 | Hours | ASTM D 1693A | (10% legpal,F50) | - |
Environmental Stress - Cracking Resistance (ESCR) : @10% Igepal Soln (F₅₀) | 40 | Hours | ASTM D 1693A | (100% legpal,F50) | - |
Thermal properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Deflection temperature under load | 52 | °C | ASTM D648 | (At 66psi-unannealed) | - |
Deflection temperature under load | 36 | °C | ASTM D648 | (At 264psi-unannealed) | - |
Peak Melting Temperature | 125 | °C | ASTM D 3418 | - | - |
Additional Information:
All physical properties were measured on 3 mm. rotomolded samples unless a different value is shown, except for ESCR, which was measured on compression molded samples.
Tensile testing was conducted at a crosshead speed of 50 mm/min. The tensile strength reported refers to the maximum stress reached during the test.
Test procedures may be modified to accommodate operating conditions or facility limitations.
Legal Statement:
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Plastic Generic Family | Polyethylene (PE) |
---|---|
Description | Additional Information: All physical properties were measured on 3 mm. rotomolded samples unless a different value is shown, except for ESCR, which was measured on compression molded samples. Tensile testing was conducted at a crosshead speed of 50 mm/min. The tensile strength reported refers to the maximum stress reached during the test. Test procedures may be modified to accommodate operating conditions or facility limitations.
Legal Statement: Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
|