Marlex® HMN TR-945G
- Chevron Phillips Chemical Company LLC
- Marlex®
- High Density Polyethylene ( HDPE )
Request Sample
Request Documents
Ask Question
Share
You`ll need an account to perform this action. Don't worry. It's free!
Sign Up
Product Reviews
Add to Compare
You`ll need an account to compare products. Don't worry. It's free!
Sign Up
HMN TR-945G Polyethylene is the high density polyethylene resin is an ethylene-hexene copolymer tailored for rotational molding applications.
You`ll need an account to add a review. Don't worry. It's free!
Sign Up
You`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Technical data sheetProduct Details
- Manufacturer
Chevron Phillips Chemical Company LLC - Brand
Marlex®
- Plastic Generic Family
Polyethylene (PE) - Plastic Generic Symbol
High Density Polyethylene ( HDPE )
Properties
Attributes
Material Status
Commercial: ActiveFeatures
Ethylene-hexene copolymer | Wide process windows | Good Impact strength | Good flow combined with fair ESCR | High modulus | Durability | 35 US mesh powderApplications
ROTO molding | Large tanks | Other high modulus parts | DuctworkPhysical Form
PowderProcessing Grades
Large tank gradeProcessing Technology
ROTO MoldingIndustry
ROTO molding industryCertifications
ASTM D4976 - PE 233 | FDA 21 CFR 177.1520(c) | Long term UV stabilization – ASTM 2565 (Cycle 1): greater than UV-21Physical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Melt Index | 6.0 | gm/10 min | ASTM D1238 | 190 °C/2.16 kg | - |
| Durometer Hardness | 63 | ASTM D2240 | Type D | - | |
| Density | 0.945 | gm/cm³ | ASTM D1505 | - | - |
Mechanical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Flexural Modulus | 740 | MPa | 1 % Secant - 16:1 span:depth, 0.5 in/min | - | |
| Flexural Modulus | 910 | MPa | Tangent - 16:1 span:depth, 0.5 in/min | - | |
| Elongation @ Break | 460 | % | 2 in/min, Type IV bar | - | |
| Tensile strength at Yield | 20 | MPa | 2 in/min, Type IV bar | - | |
| Environmental Stress - Cracking Resistance (ESCR) : @10% Igepal Soln (F₅₀) | 25 | Hours | ASTM D1693 | - | - |
| Environmental Stress - Cracking Resistance (ESCR) : @10% Igepal Soln (F₅₀) | 70 | Hours | ASTM D1693 | - | - |
Impact Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Impact Strength | 92 | J | ARM Impact | 1/8" (3.2 mm) thickness, -40 °C | - |
| Impact Strength | 223 | J | ARM Impact | 1/4" (6.35 mm) thickness, -40 °C | - |
Thermal properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| VICAT Softening Point | 118 | °C | ASTM D1525 | Loading 1, Rate A | - |
| Brittleness Temperature | -75 | °C | ASTM D746 | Type A, Type I specimen | - |
| Melting Temperature | 130 | °C | ASTM D 3418 | - | - |
| Crystallization Temperature | 113 | °C | ASTM D 3418 | - | - |
| Heat Deflection temperature | 64 | °C | ASTM D648 | 66 psi, Method A | - |
| Heat Deflection temperature | 44 | °C | ASTM D648 | 264 psi, Method A | - |
| Plastic Generic Family | Polyethylene (PE) |
|---|---|
| Plastic Generic Symbol (Sub Group) | HDPE Prime / Virgin Resin |
| Material Status | Commercial: Active |
| Features | 35 US mesh powder, Durability, Ethylene-hexene copolymer, Good flow combined with fair ESCR, Good Impact strength, High modulus, Wide process windows |
| Applications | Ductwork , Large tanks, Other high modulus parts , ROTO molding |
| Physical Form | Powder |
| Processing Grades | Large tank grade |
| Processing Technology | ROTO Molding |
| Industry | ROTO molding industry |
| Certifications | ASTM D4976 - PE 233 , FDA 21 CFR 177.1520(c) , Long term UV stabilization – ASTM 2565 (Cycle 1): greater than UV-21 |