Nexxstar™ Low EVA-00111
- ExxonMobil Chemical
You`ll need an account to perform this action. Don't worry. It's free!
Sign UpNexxstar™ Low EVA-00111 resin is a copolymer of ethylene and vinyl acetate.
You`ll need an account to add a review. Don't worry. It's free!
Sign UpYou`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Product Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Film Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Tensile Strength at Yield TD | 6.5 | MPa | ASTM D882 | - | - |
Puncture Energy | 2.8 | J | EXXONMOBIL Method | - | - |
Puncture Force | 67 | N | EXXONMOBIL Method | - | - |
Elmendorf Tear Strength TD | 60 | gm | ASTM D1922 | - | - |
Elmendorf Tear Strength MD | 190 | gm | ASTM D1922 | - | - |
Secant Modulus TD - 1% Secant | 130 | MPa | ASTM D882 | - | - |
Secant Modulus MD - 1% Secant | 110 | MPa | ASTM D882 | - | - |
Elongation at Break TD | 620 | % | ASTM D882 | - | - |
Elongation at Break MD | 200 | % | ASTM D882 | - | - |
Tensile Strength at Break TD | 29 | MPa | ASTM D882 | - | - |
Tensile Strength at Break MD | 34 | MPa | ASTM D882 | - | - |
Tensile Strength at Yield MD | 9.8 | MPa | ASTM D882 | - | - |
Physical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Density | 0.928 | gm/cm³ | ASTM D1505 | - | - |
Melt Flow Index | 0.50 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
Vinyl Acetate Content | 7.5 | wt % | EXXONMOBIL Method | - | - |
Optical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Gloss @ 45° | 52 | ASTM D2457 | - | - | |
Haze | 9.4 | % | ASTM D1003 | - | - |
Impact Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Dart Drop Impact | 360 | gm | ASTM D 1709/A | - | - |
Thermal properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Peak Melting Temperature | 100 | °C | EXXONMOBIL Method | - | - |
VICAT Softening Point | 80.0 | °C | EXXONMOBIL Method | - | - |
Legal Statement:
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement:
Film (1.5 mil/38.1 micron) made from Nexxstar™ Low EVA-00111 resin on a 2.5 inch (63.5 mm) blown film line with a 2.5:1 blow-up ratio, a melt temperature of 325-345°F (163-174°C), a 30 mil
(0.76 mm) die gap at a rate of 8 lbs/hr/in die circumference (1.43 kg/hr/cm).
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Plastic Generic Family | Polyethylene (PE) |
---|---|
Description | Legal Statement: Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement:
Film (1.5 mil/38.1 micron) made from Nexxstar™ Low EVA-00111 resin on a 2.5 inch (63.5 mm) blown film line with a 2.5:1 blow-up ratio, a melt temperature of 325-345°F (163-174°C), a 30 mil (0.76 mm) die gap at a rate of 8 lbs/hr/in die circumference (1.43 kg/hr/cm).
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
|