ULTRA AD 0433EH2
- ExxonMobil Chemical
You`ll need an account to perform this action. Don't worry. It's free!
Sign UpAD 0433EH2 is a copolymer of ethylene and vinyl acetate.
You`ll need an account to add a review. Don't worry. It's free!
Sign UpYou`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Product Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Physical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Density | 0.954 | gm/cm³ | ASTM D1505 | - | - |
Melt Flow Index | 400 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
Vinyl Acetate Content | 33.0 | wt % | EXXONMOBIL Method | - | - |
Mechanical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Tensile Modulus | 7.1 | MPa | ASTM D638 | (0.20 in/min(5.0mm/min)) | - |
Tensile strength at Break | 1.8 | MPa | ASTM D638 | (20 in/min(500mm/min)) | - |
Elongation @ Break | 780 | % | ASTM D638 | (20 in/min(500mm/min)) | - |
Thermal properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Peak Melting Temperature | 61 | °C | EXXONMOBIL Method | - | - |
Legal Statement:
Tris(nonylphenol)phosphite (TNPP) CAS# 26523-78-4 is not intentionally used by ExxonMobil in this product. Although this product is not routinely tested for its presence, based on product composition knowledge this substance is not expected to be present. However, the fact that this substance is not intentionally used by ExxonMobil in this product does not exclude that trace levels of this substance may be present as a result of the specific characteristics of the raw materials and/or of the manufacturing process.
This product is not intended for use in medical applications and should not be used in any such applications.
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
Processing Statement:
Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D 4703 Procedure C (Tensile ASTM D 638 : Type IV
dumbbell).
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Value reported is an estimate based on ExxonMobil's correlation from melt flow rate data measured at other standard conditions, based on ASTM D 1238.
Plastic Generic Family | Polyethylene (PE) |
---|---|
Description | Legal Statement: Tris(nonylphenol)phosphite (TNPP) CAS# 26523-78-4 is not intentionally used by ExxonMobil in this product. Although this product is not routinely tested for its presence, based on product composition knowledge this substance is not expected to be present. However, the fact that this substance is not intentionally used by ExxonMobil in this product does not exclude that trace levels of this substance may be present as a result of the specific characteristics of the raw materials and/or of the manufacturing process. This product is not intended for use in medical applications and should not be used in any such applications.
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
Processing Statement: Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D 4703 Procedure C (Tensile ASTM D 638 : Type IV dumbbell).
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Value reported is an estimate based on ExxonMobil's correlation from melt flow rate data measured at other standard conditions, based on ASTM D 1238.
|