ULTRA FL 00206
- ExxonMobil Chemical
Request Sample
Request Documents
Ask Question
Share
You`ll need an account to perform this action. Don't worry. It's free!
Sign Up
You`ll need an account to compare products. Don't worry. It's free!
Sign Up
FL 00206 is a copolymer of ethylene and vinyl acetate.
You`ll need an account to add a review. Don't worry. It's free!
Sign Up
You`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Technical data sheetProduct Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Physical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Density | 0.926 | gm/cm³ | ASTM D1505 | - | - |
| Melt Flow Index | 2.5 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
| Vinyl Acetate Content | 6.5 | wt % | EXXONMOBIL Method | - | - |
| Durometer Hardness | 96 | Shore A | ASTM D2240 | - | - |
| Durometer Hardness | 39 | Shore D | ASTM D2240 | - | - |
Mechanical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Tensile Modulus | 130 | MPa | ASTM D638 | (0.20 in/min(5.0mm/min)) | - |
| Tensile strength at Break | 14 | MPa | ASTM D638 | (20 in/min(500mm/min)) | - |
| Elongation @ Break | 740 | % | ASTM D638 | (20 in/min(500mm/min)) | - |
Thermal properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Peak Melting Temperature | 99 | °C | EXXONMOBIL Method | - | - |
| VICAT Softening Point | 79 | °C | ASTM D1525 | - | - |
Legal Statement:
This product is not intended for use in medical applications and should not be used in any such applications.
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
Processing Statement:
Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D 4703 Procedure C (Tensile ASTM D 638 : Type IV dumbbell, Hardness ASTM D 2240 : 3 plied up disks).
Processing temperatures above 280 °C (536 °F) may cause resin degradation. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
| Plastic Generic Family | Polyethylene (PE) |
|---|---|
| Description | Legal Statement: This product is not intended for use in medical applications and should not be used in any such applications.
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
Processing Statement: Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D 4703 Procedure C (Tensile ASTM D 638 : Type IV dumbbell, Hardness ASTM D 2240 : 3 plied up disks). Processing temperatures above 280 °C (536 °F) may cause resin degradation. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
|