ULTRA FL 00209
- ExxonMobil Chemical
You`ll need an account to perform this action. Don't worry. It's free!
Sign UpFL 00209 is a copolymer of ethylene and vinyl acetate. Processing Conditions Processing temperatures above 270 °C (518 °F) may cause resin degradation.
Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.
You`ll need an account to add a review. Don't worry. It's free!
Sign UpYou`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Product Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Film Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Tensile Strength at Break TD | 26 | MPa | ASTM D882 | - | - |
Elongation at Break MD | 510 | % | ASTM D882 | - | - |
Elongation at Break TD | 650 | % | ASTM D882 | - | - |
Secant Modulus MD - 1% Secant | 97 | MPa | ASTM D882 | - | - |
Secant Modulus TD - 1% Secant | 100 | MPa | ASTM D882 | - | - |
Elmendorf Tear Strength MD | 110 | gm | ASTM D1922 | - | - |
Elmendorf Tear Strength TD | 170 | gm | ASTM D1922 | - | - |
Tensile Strength at Break MD | 30 | MPa | ASTM D882 | - | - |
Physical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Density | 0.931 | gm/cm³ | ASTM D1505 | - | - |
Durometer Hardness | 94 | Shore A | ASTM D2240 | (15 sec) | - |
Vinyl Acetate Content | 9.4 | wt % | EXXONMOBIL Method | - | - |
Melt Flow Index | 2.1 | gm/10 min | ASTM D1238 | (190°C / 21.6 Kg) | - |
Mechanical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Tensile Modulus | 110 | MPa | ASTM D638 | (0.20 in/min(5.0mm/min)) | - |
Elongation @ Break | >100 | % | ASTM D638 | (20 in/min(500mm/min)) | - |
Impact Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Dart Drop Impact | 370 | gm | ASTM D 1709/A | - | - |
Thermal properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Peak Melting Temperature | 99 | °C | EXXONMOBIL Method | - | - |
VICAT Softening Point | 78 | °C | EXXONMOBIL Method | - | - |
Legal Statement:
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement:
Film properties were measured on a 50µm (1.97 mil) thick film extruded on a conventional LDPE extruder (screw diameter 60mm (2.36 in), rotating die diameter : 200mm (7.87 in), die gap : 1
mm (39.4mil), BUR 2.5:1, die temperature 180°C (356°F)). Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D 4703
Procedure C (tensile ASTM D 638 : Type IV dumbbell, hardness ASTM D 2240 : 3 plied up disks).
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Plastic Generic Family | Polyethylene (PE) |
---|---|
Description | Legal Statement: Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement: Film properties were measured on a 50µm (1.97 mil) thick film extruded on a conventional LDPE extruder (screw diameter 60mm (2.36 in), rotating die diameter : 200mm (7.87 in), die gap : 1 mm (39.4mil), BUR 2.5:1, die temperature 180°C (356°F)). Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D 4703 Procedure C (tensile ASTM D 638 : Type IV dumbbell, hardness ASTM D 2240 : 3 plied up disks).
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
|