FL 00218 is a copolymer of ethylene and vinyl acetate offering low gel. Processing Conditions Processing temperatures above 240 °C (464 °F) may cause resin
degradation. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.
You`ll need an account to add a review. Don't worry. It's free!
Sign Up
You`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Technical data sheetProduct Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Film Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Tensile Strength at Break MD | 37 | MPa | ASTM D882 | - | - |
| Tensile Strength at Break TD | 36 | MPa | ASTM D882 | - | - |
| Elongation at Break MD | 550 | % | ASTM D882 | - | - |
| Elongation at Break TD | 720 | % | ASTM D882 | - | - |
| Secant Modulus MD - 1% Secant | 48 | MPa | ASTM D882 | - | - |
| Secant Modulus TD - 1% Secant | 52 | MPa | ASTM D882 | - | - |
| Elmendorf Tear Strength MD | 70 | gm | ASTM D1922 | - | - |
| Elmendorf Tear Strength TD | 170 | gm | ASTM D1922 | - | - |
Physical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Density | 0.940 | gm/cm³ | ASTM D1505 | - | - |
| Melt Flow Index | 1.7 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
| Vinyl Acetate Content | 18.0 | wt % | EXXONMOBIL Method | - | - |
Impact Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Dart Drop Impact | 660 | gm | ASTM D 1709/A | - | - |
Thermal properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Peak Melting Temperature | 87 | °C | EXXONMOBIL Method | - | - |
| VICAT Softening Point | 62 | °C | EXXONMOBIL Method | - | - |
Legal Statement:
This product is not intended for use in medical applications and should not be used in any such applications.
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
Processing Statement:
Film properties were measured on a 50µm (1.97 mil) thick film extruded on a conventional LDPE extruder (screw diameter 60mm (2.36 in), rotating die diameter :
200mm (7.87 in), die gap : 1 mm (39.4mil), BUR 2.5:1, die temperature 180°C (356°F)).
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
| Plastic Generic Family | Polyethylene (PE) |
|---|---|
| Description | Legal Statement: This product is not intended for use in medical applications and should not be used in any such applications.
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
Processing Statement: Film properties were measured on a 50µm (1.97 mil) thick film extruded on a conventional LDPE extruder (screw diameter 60mm (2.36 in), rotating die diameter :
200mm (7.87 in), die gap : 1 mm (39.4mil), BUR 2.5:1, die temperature 180°C (356°F)).
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
|