ULTRA FL 00728CC
- ExxonMobil Chemical
You`ll need an account to perform this action. Don't worry. It's free!
Sign UpFL 00728CC is an excellent coextrusion partner in extrusion coating, blown and cast film. Good adhesion onto OPP in coextrusion. This grade offers excellent
opticals, low gel and a very low Seal Initiation Temperature in sealing applications. Processing Conditions Excellent results are obtained in extrusion coating at 200 °C
(392°F) temperature range. Processing temperatures above 220°C (428°F) may cause resin degradation. FL00728CC should be fed into the extruder after LDPE of a
similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.
You`ll need an account to add a review. Don't worry. It's free!
Sign UpYou`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Product Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Physical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Density | 0.951 | gm/cm³ | ASTM D1505 | - | - |
Melt Flow Index | 7.0 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
Vinyl Acetate Content | 27.5 | wt % | EXXONMOBIL Method | - | - |
Durometer Hardness | 80 | Shore A | ASTM D2240 | (15 sec) | - |
Durometer Hardness | 25 | Shore D | ASTM D2240 | (15 sec) | - |
Mechanical Properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Tensile Modulus | 16 | MPa | ASTM D638 | (0.20 in/min(5.0mm/min)) | - |
Tensile strength at Break | 12 | MPa | ASTM D638 | (20 in/min(500mm/min)) | - |
Elongation @ Break | 890 | % | ASTM D638 | (20 in/min(500mm/min)) | - |
Thermal properties
Title | Value | Unit | Method | Additional Information | Property Notes |
---|---|---|---|---|---|
Peak Melting Temperature | 71 | °C | EXXONMOBIL Method | - | - |
VICAT Softening Point | 43 | °C | EXXONMOBIL Method | - | - |
Legal Statement:
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement:
Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D4703 Procedure C (Tensile ASTM D638 : Type IV dumbbell, Hardness
ASTM D2240 : 3 plied up disks) and 4 mm (157 mil) for VICAT.
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Value reported is an estimate based on ExxonMobil's correlation from melt flow rate data measured at other standard conditions, based on ASTM D 1238.
Plastic Generic Family | Polyethylene (PE) |
---|---|
Description | Legal Statement: Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement:
Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D4703 Procedure C (Tensile ASTM D638 : Type IV dumbbell, Hardness
ASTM D2240 : 3 plied up disks) and 4 mm (157 mil) for VICAT.
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Value reported is an estimate based on ExxonMobil's correlation from melt flow rate data measured at other standard conditions, based on ASTM D 1238. |