FL 02020 is primarily designed for high speed/low coating weight extrusion coating and is a good coextrusion partner with other polymers. FL 02020 is an
excellent sealing material with a very low seal initiation temperature, high clarity, and low gel. Excellent results are obtained in extrusion coating at 220°C
(428°F) temperature range. Processing temperatures above 240°C (464°F) may cause resin degradation. FL 02020 should be fed into the extruder after LDPE of a
similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.
You`ll need an account to add a review. Don't worry. It's free!
Sign Up
You`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Technical data sheetProduct Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Physical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Density | 0.940 | gm/cm³ | ASTM D1505 | - | - |
| Melt Flow Index | 20 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
| Vinyl Acetate Content | 20.0 | wt % | EXXONMOBIL Method | - | - |
| Durometer Hardness | 87 | Shore A | ASTM D2240 | (15 sec) | - |
| Durometer Hardness | 29 | Shore D | ASTM D2240 | (15 sec) | - |
Mechanical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Tensile Modulus | 31 | MPa | ASTM D638 | (0.20 in/min(5.0mm/min)) | - |
| Tensile strength at Break | 8.2 | MPa | ASTM D638 | (20 in/min(500mm/min)) | - |
| Elongation @ Break | 830 | % | ASTM D638 | (20 in/min(500mm/min)) | - |
Thermal properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Peak Melting Temperature | 80 | °C | EXXONMOBIL Method | - | - |
| VICAT Softening Point | 48 | °C | EXXONMOBIL Method | - | - |
Legal Statement:
This product is not intended for use in medical applications and should not be used in any such applications.
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
Processing Statement:
Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D4703 Procedure C (Tensile ASTM D638 : Type IV dumbbell, Hardness ASTM
D2240 : 3 plied up disks) and 4 mm (157 mil) for VICAT.
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Value reported is an estimate based on ExxonMobil's correlation from melt flow rate data measured at other standard conditions, based on ASTM D1238.
| Plastic Generic Family | Polyethylene (PE) |
|---|---|
| Description | Legal Statement: This product is not intended for use in medical applications and should not be used in any such applications. Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
Processing Statement: Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D4703 Procedure C (Tensile ASTM D638 : Type IV dumbbell, Hardness ASTM D2240 : 3 plied up disks) and 4 mm (157 mil) for VICAT. Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Value reported is an estimate based on ExxonMobil's correlation from melt flow rate data measured at other standard conditions, based on ASTM D1238. |