UL 00226CC is a copolymer of ethylene and vinyl acetate. Processing Conditions Processing temperatures above 230 °C (446 °F) may cause resin degradation.
You`ll need an account to add a review. Don't worry. It's free!
Sign Up
You`ll need to place an order to add a review. Don't worry. It's easy!
Documents
Technical data sheetProduct Details
- Manufacturer
ExxonMobil Chemical
- Plastic Generic Family
Polyethylene (PE)
Properties
Physical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Density | 0.950 | gm/cm³ | ASTM D1505 | - | - |
| Melt Flow Index | 2.0 | gm/10 min | ASTM D1238 | (190°C / 2.16 Kg) | - |
| Vinyl Acetate Content | 26.0 | wt % | EXXONMOBIL Method | - | - |
| Durometer Hardness | 82 | Shore A | ASTM D2240 | (15 sec) | - |
| Durometer Hardness | 28 | Shore D | ASTM D2240 | (15 sec) | - |
Mechanical Properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Tensile Modulus | 20 | MPa | ASTM D638 | (0.20 in/min(5.0mm/min)) | - |
| Tensile strength at Break | 19 | MPa | ASTM D638 | (20 in/min(500mm/min)) | - |
| Elongation @ Break | 860 | % | ASTM D638 | (20 in/min(500mm/min)) | - |
Thermal properties
| Title | Value | Unit | Method | Additional Information | Property Notes |
|---|---|---|---|---|---|
| Peak Melting Temperature | 74 | °C | EXXONMOBIL Method | - | - |
| VICAT Softening Point | 46 | °C | ASTM D1525 | - | - |
Legal Statement:
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement:
Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D4703 Procedure C (Tensile ASTM D638 : Type IV
dumbbell, Hardness ASTM D2240 : 3 plied up disks) and 4 mm (157 mil) for VICAT.
Notes:
Typical properties: these are not to be construed as specifications.
Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Value reported is an estimate based on ExxonMobil's correlation from melt flow rate data measured at other standard conditions, based on ASTM D 1238.
| Plastic Generic Family | Polyethylene (PE) |
|---|---|
| Description | Legal Statement: Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EU, HPFB).
This product is not intended for use in medical applications and should not be used in any such applications.
Processing Statement: Molded properties were measured on 2 mm (78.7 mil) thick compression molded plaques prepared based on ASTM D4703 Procedure C (Tensile ASTM D638 : Type IV dumbbell, Hardness ASTM D2240 : 3 plied up disks) and 4 mm (157 mil) for VICAT.
Notes: Typical properties: these are not to be construed as specifications. Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
Value reported is an estimate based on ExxonMobil's correlation from melt flow rate data measured at other standard conditions, based on ASTM D 1238. |